冯钟潮
,
郭良
,
梁勇
,
韩健
,
侯万良
,
宁小光
金属学报
用大功率(kW级)CO_2激光在金属基材上通过化学气相沉积获得α-Si_3N_4膜。膜层多为细小的Si_3N_4颗粒组成,与基材有良好的结合,具有超硬和优良的耐磨抗蚀等性能,厚度在5—30μm范围内可控。
关键词:
激光化学气相沉积
,
Si_3N_4 film
,
microstructure
,
hardness
,
wear resistance
,
corrosion resistance
侯建强，符寒光，蒋业华，周荣，岑启宏
钢铁研究学报
设计了5种高速钢轧辊材料，利用光学显微镜(OM)、扫描电镜(SEM)、X射线衍射(XRD)等分析手段，并通过硬度测试、冲击韧性试验和磨损试验，对含硼低合金高速钢轧辊材料在铸态、回火后的组织与性能及其耐磨性进行了系统研究。结果表明，含硼低合金高速钢轧辊材料铸态组织包括马氏体基体、残余奥氏体和不同种类的碳硼化合物，其铸态硬度大于HRC 64，碳硼化合物沿晶界呈网状分布。经RE-Mg-Ti复合变质处理后，晶界出现明显的颈缩和断网。对轧辊材料进行回火发现，随着回火温度的升高，轧辊硬度逐渐降低。相同条件下，未变质轧辊材料的韧性较变质轧辊材料韧性略低，加入过量的变质剂反而降低轧辊材料的韧性。磨损试验发现，经RE-Mg-Ti复合变质的含硼高速钢的耐磨性大于对比试样高碳高钒高速钢的耐磨性。
关键词:
高速钢轧辊
,
boron alloying
,
modification
,
tempering
,
wear resistance
吴萍
,
周昌炽
,
唐西南
金属学报
利用预涂敷与激光重熔方法制备陶瓷梯度涂层，并对涂层的冶金结构、组成、硬度、以及耐磨性进行分析。结果表明：该涂层内陶瓷硬质相体积百分比沿基体到表面方向呈梯度变化，过渡层为具有良好韧性的固溶体。涂层结构均匀，和基体结合良好，无气孔和裂纹。厚度为０．４－０．８ｍｍ，表层硬度达ＨＶ_（０．２）１１００。与普通激光涂层比较，涂层内部的硬度随着成分组成的变化而平缓变化，既提高了涂层与基体的结合强度又提高了表面的耐磨性，同时，避免裂纹的产生。
关键词:
激光合金化
,
graded coating
,
ceramic
,
wear resistance
张福成
,
罗海辉
,
RobertsSteve-G
,
ToddRichard-I
无机材料学报
doi:10.3724/SP.J.1077.2007.00493
通过磨粒磨损试验测定了氧化铝 陶瓷、氧化铝/碳化硅复合陶瓷和氧化铝/莫来石复合陶瓷的耐磨性. 利用透射电子显微镜(TEM)观察了样品的微观结构, 采用扫描电子显微镜(SEM)分析了样品的断口形貌和磨损表面的剥落情况. 研究了断裂方式对磨损表面剥落和耐磨性的影响. 结果表明: 氧化铝陶瓷的磨损主要由断裂磨损机制控制, 氧化铝/碳化硅复合陶瓷的磨损主要由塑性磨损机制控制, 氧化铝/莫来石复合陶瓷受这两种磨损机制共同作用. 相对于氧化铝陶瓷, 氧化铝/碳化硅复合陶瓷和氧化铝/莫来石复合陶瓷的耐磨性提高2～4倍, 这主 要是由于其断裂方式转变为以穿晶断裂为主, 减少了磨损面的脆性剥落.
关键词:
氧化铝
,
ceramic composite
,
wear resistance
,
fracture mode
Q. Y Pan
,
WD. Huang
,
YM. Li
,
X. Lin
,
YH. Zhou and X.C. Yan( State Key Lab. of Solidification Processing
,
Northwestern Polytechnical University
,
Xi'an 710072
,
China ( Laser Processing Center
,
Tianjin College of Textile Technology
,
Tianjin 300160
,
China )
金属学报(英文版)
A novel wide-band laser cladding system, with high rate of cladding, has been developed in the present work. The system mainly consisted of a 5kW CO2 laser, an automatic Fowder feeder and a wide-band scanning rotative polygon mirmr which can produce a linear or rectangular focused laser beam. Using this system, a Ni-Cr-Si-B alloy powder was cladded on the sudece of tgpe 321 austenitic stainless steel in onder to improve its wear and cormsion resistance. The pitting cormsion, high temperuture oxidation and wear tests were conducted in onder to evaluate the propertles of the laser cladded layer. The results demonstrated that the cladded layer can significantly improtte the adhesive wear and pitting cormsion resistance of the substmte. Moreover,the cladded layer exhibited good oxidafion resistance, which is almost the same as that of GMR-235D N-based superalloy.
关键词:
austenitic stainless steel
,
null
,
null
,
null
刘莎莎
,
王宇航
,
张维平
稀有金属材料与工程
利用横流CO2激光器在TA15钛合金表面通过优化的激光熔覆工艺制备出原位自生的多种颗粒增强钴基复合涂层,以增强表面的耐磨性和硬度.利用X射线衍射(XRD)、金相、扫描电镜(SEM)、硬度测试机和磨损试验机等方法对熔覆层进行分析.结果表明,熔覆层的显微结构主要由γ-Co、α-Ti固溶体和弥散分布的原位自生TiB2,、Cr5Si3,、TiC、WB、SiC、Co3Ti、NiC颗粒组成,这些多种颗粒增强相弥散分布在细小的树枝晶组织之间.熔覆层的显微硬度比基体提高很多,HV达到10000 MPa左右,约为基体硬度的3倍.与钛合金相比,熔覆层的耐磨性也有显著提高,其磨损率约为钛合金的1/12.熔覆层的磨损机理具有粘着磨损和磨粒磨损的混合特征.
关键词:
钛合金
,
激光熔覆
,
耐磨性
,
显微组织
,
显微硬度